Several tips on welding equipment, MIG and TIG welders, plasma cutters. When appearance counts, TIG welding creates a high quality, clean weld that is far less likely to distort the metal by using a nonconsumable tungsten electrode. There is no need to worry about splatter because it only uses the necessary amount of filler metal needed in the welding puddle, making for the highest quality weld in every respect. However, TIG is fairly specialized and requires a good deal of training in order to master it—so make sure any TIG welder purchase is paired with a plan to take welding classes. Instead of the point and shoot simplicity of MIG welding, TIG requires the use of a foot pedal to regulate the welding process. A filler rod that is separate from the torch that must be fed in gradually. Many professional welders prefer TIG because it can weld a wide variety of metals and because of the versatility of argon gas used during TIG welding. There is no slag to block the view of the weld puddle. Argon gas can weld any metal at any thickness with TIG welding, and therefore there is no need to change the gas depending on the project.

Best welding handbook: how to become a more skilled welder and how to pick the best welding equipment. Use the smallest tungsten that will get the job done. Use the smallest tungsten to get the job done. …within reason. Another way of saying this is don’t just use a 1/8” electrode for everything. There are jobs where a 1/8” electrode is great like for welding 3/16” thick aluminum. But what if you are welding on the edge of a .030” turbine blade? A .040” electrode will be plenty to handle the 15 amps and will give much better starts than even a 1/16” electrode. Too large an electrode can cause an erratic arc and contamination…and A bad start where the high frequency tries to arc up inside the cup and off the side of the tungsten can easily melt off a thin edge and scrap an expensive part. 2% thoriated or lanthanated tungsten electrodes hold up at high amperage better than most all other electrodes. When welding at higher amperages, often times you can use one size smaller electrode by using 2% thoriated or lanthanated. And that is a good thing.

Many companies get completely “bogged down” in the paperwork required to run a business. But with today’s latest technological advances, there are items that can be a great help. For instance, Lincoln Electric offers something called ArcWorks software which can document procedures, create drawings everyone in the shop can access, keep track of welding operator’s qualifications, and many other things. Software such as this can be tailored to the individual company’s needs and provide great efficiencies and also eliminate mistakes. Adding Robotics or Hard Automation to the Operation: Today’s technological advances offer many options. Robotics can be justified when the volume of parts a company produces is so great that it can offset the monies spent on a robot. Robotics can also be considered if there are a number of different parts that are similar enough in nature to be able to be handled by the same robot. If robots are not justified, a company might determine that fixturing or hard automation could be used to increase efficiency or quality. One company incorporated fixturing and clamps to hold down a tank while the seam was being welded. In another case, an automotive manufacturer decided that automation was necessary because of the amount of parts and intricate angles and welding positions. Looking for the best Welding Supplies? We recommend Welding Supplies Direct & associated company TWS Direct Ltd is an online distributor of a wide variety of welding supplies, welding equipment and welding machine. We supply plasma cutters, MIG, TIG, ARC welding machines and support consumables to the UK, Europe and North America.

So pay attention to the way you grind your tungsten. You have probably read that Tungsten electrodes should only be ground longitudinally, not sideways or the world will come to an end and dogs and cats will start sleeping together. Take it from someone who has been TIG welding for over 30 years and has sharpened electrodes every way imaginable including using a cutting torch. That’s right I said cutting torch. It does matter how you grind tungsten electrodes. There is a big difference between a tungsten electrode ground sideways on a 36 grit stone to one ground properly on a fine diamond wheel. But there is not much difference between a tungsten ground sideways on a fine wheel and one that has been ground longitudinally on the same wheel… Unless you are welding razor blades or at extremely low amperages. or doing automatic low amperage orbital welding. A lot of people will argue this point with me. I dont care. I cant make myself say that tungsten grinders make a lot of difference when I dont really believe it.

The welding setup, welder settings, and electrode selection will impact how fast welders can work. Industrial welders invest time in planning the size and shape of their welding areas, how parts are laid out, and how they supply their shielding gas. Testing settings or an electrode on a piece of scrap metal, especially for a beginners, will save time in the long run. Learn more about setting up an efficient shop here. Welding Downhill Increases Welding Speed: While welding downhill is a faster way to weld, it’s not as strong as welding uphill. On most projects it’s not worth sacrificing strength and durability for the sake of welding speed. However, if the metal is thin enough, then welding downhill won’t make the weld weaker and may even be the correct technique for the job. Learn about uphill and downhill welding and see these diagrams of vertical and downhill welding.

For the best control of your weld bead, keep the wire directed at the leading edge of the weld pool. When welding out of position (vertical, horizontal or overhead welding), keep the weld pool small for best weld bead control, and use the smallest wire diameter size you can. A bead that is too tall and skinny indicates a lack of heat into the weld joint or too fast of travel speed. Conversely, if the bead is flat and wide, the weld parameters are too hot or you are welding too slowly. Ideally, the weld should have a slight crown that just touches the metal around it. Keep in mind that a push technique preheats the metal, which means this is best used with thinner metals like aluminum. On the other hand, if you pull solid wire, it flattens the weld out and puts a lot of heat into the metal. Finally, always store and handle your filler metals properly. Keep product in a dry, clean place — moisture can damage wire and lead to costly weld defects, such as hydrogen-induced cracking. Also, always use gloves when handling wires to prevent moisture or dirt from your hands settling on the surface. When not in use, protect spools of wire by covering them on the wire feeder, or better yet, remove the spool and place it in a clean plastic bag, closing it securely.

All welding requires the application of heat, which melts the metal being welded. With the TIG process, the heat comes from an electric arc that streams between the electrode in a hand-held torch and the metal being welded. The arc and molten metal are shielded by an inert gas, which protects the electrode and base metal from oxidizing. Filler rod is usually added to the puddle of molten metal as the weld progresses. The essence of making a good weld is heat control, which is governed by how you modulate the arc as it streams from the torch. Let’s look at this in detail. Source: https://www.weldingsuppliesdirect.co.uk/.